Physics – Condensed Matter – Materials Science
Scientific paper
2010-11-05
Phys. Rev. B 82, 036604 (2010)
Physics
Condensed Matter
Materials Science
Scientific paper
We report resonant ultrasound spectroscopy (RUS), dilatometry/magnetostriction, magnetotransport, magnetization, specific heat, and $^{119}$Sn M\"ossbauer spectroscopy measurements on SnTe and Sn$_{0.995}$Cr$_{0.005}$Te. Hall measurements at $T=77$ K indicate that our Bridgman-grown single crystals have a $p$-type carrier concentration of $3.4 \times 10^{19}$ cm$^{-3}$ and that our Cr-doped crystals have an $n$-type concentration of $5.8 \times 10^{22}$ cm$^{-3}$. Although our SnTe crystals are diamagnetic over the temperature range $2\, \text{K} \leq T \leq 1100\, \text{K}$, the Cr-doped crystals are room temperature ferromagnets with a Curie temperature of 294 K. For each sample type, three-terminal capacitive dilatometry measurements detect a subtle 0.5 micron distortion at $T_c \approx 85$ K. Whereas our RUS measurements on SnTe show elastic hardening near the structural transition, pointing to co-elastic behavior, similar measurements on Sn$_{0.995}$Cr$_{0.005}$Te show a pronounced softening, pointing to ferroelastic behavior. Effective Debye temperature, $\theta_D$, values of SnTe obtained from $^{119}$Sn M\"ossbauer studies show a hardening of phonons in the range 60--115K ($\theta_D$ = 162K) as compared with the 100--300K range ($\theta_D$ = 150K). In addition, a precursor softening extending over approximately 100 K anticipates this collapse at the critical temperature, and quantitative analysis over three decades of its reduced modulus finds $\Delta C_{44}/C_{44}=A|(T-T_0)/T_0|^{-\kappa}$ with $\kappa = 0.50 \pm 0.02 $, a value indicating a three-dimensional softening of phonon branches at a temperature $T_0 \sim 75$ K, considerably below $T_c$. We suggest that the differences in these two types of elastic behaviors lie in the absence of elastic domain wall motion in the one case and their nucleation in the other.
Cooley J. C.
Fisher Russell A.
Gubernatis James E.
Lashley J. C.
Littlewood Peter B.
No associations
LandOfFree
Tin telluride: a weakly co-elastic metal does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.
If you have personal experience with Tin telluride: a weakly co-elastic metal, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Tin telluride: a weakly co-elastic metal will most certainly appreciate the feedback.
Profile ID: LFWR-SCP-O-455081