Titanium additions to MgB2 conductors

Details Titanium additions to MgB2 conductors Titanium additions to MgB2 conductors

2003-02-12

arxiv.org/abs/cond-mat/0302245v1

Physics

Condensed Matter

Superconductivity

10 pages, 6 figures

Scientific paper

10.1016/S0921-4534(03)00863-3

A series of doping experiments are reported for MgB2 conductors that have been synthesized using doped boron fibers prepared by chemical vapor deposition(CVD) methods. Undoped MgB2 samples prepared from CVD prepared fibers consistently give critical current densities, Jc, in the range of 500,000 A/cm^2 in low field at 5K. These values fall by a factor of about 100 as the magnetic field increases to 3T. For heavily Ti-doped boron fibers where the B/Ti ratio is comparable to 1, there is a substantial suppression of both Tc, superconducting volume fraction, and Jc values. If, however, a sample with a few percent Ti in B is deposited on a carbon coated SiC substrate and reacted at 1100 degrees C for 15 min, then Tc is suppressed only a couple of degrees Kelvin and critical current densities are found to be approximately 2-5 x 10^6 A/cm^2 for superconducting layers ranging from 4-10 micrometers thick. These materials show Jc values over 10,000 A/cm^2 at 25K and 1.3 T.

Affiliated with

Also associated with

No associations

Rating

Titanium additions to MgB2 conductors does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with Titanium additions to MgB2 conductors, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Titanium additions to MgB2 conductors will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFWR-SCP-O-332776