Synthesis and magnetic properties of NiFe_{2-x}Al_{x}O_{4} nanoparticles

Physics – Condensed Matter – Materials Science

Scientific paper

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

24 pages, 6 figures

Scientific paper

10.1016/j.jmmm.2007.03.204

Nanocrystalline Al-doped nickel ferrite powders have been synthesized by sol-gel auto-ignition method and the effect of non-magnetic aluminum content on the structural and magnetic properties has been studied. The X-ray diffraction (XRD) revealed that the powders obtained are single phase with inverse spinel structure. The calculated grain sizes from XRD data have been verified using transmission electron microscopy (TEM). TEM photographs show that the powders consist of nanometer-sized grains. It was observed that the characteristic grain size decreases from 29 to 6 nm as the non-magnetic Al content increases, which was attributed to the influence of non-magnetic Al concentration on the grain size. Magnetic hysteresis loops were measured at room temperature with a maximum applied magnetic field of 1T. As aluminum content increases, the measured magnetic hysteresis curves become more and more narrow and the saturation magnetization and remanent magnetization both decreased. The reduction of agnetization compared to bulk is a consequence of spin non-collinearity. Further reduction of magnetization with increase of aluminum content is caused by non-magnetic Al^{3+} ions and weakened interaction between sublattices. This, as well as the decrease in hysteresis was understood in terms of the decrease in particle size.

No associations

LandOfFree

Say what you really think

Search LandOfFree.com for scientists and scientific papers. Rate them and share your experience with other people.

Rating

Synthesis and magnetic properties of NiFe_{2-x}Al_{x}O_{4} nanoparticles does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with Synthesis and magnetic properties of NiFe_{2-x}Al_{x}O_{4} nanoparticles, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Synthesis and magnetic properties of NiFe_{2-x}Al_{x}O_{4} nanoparticles will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFWR-SCP-O-281731

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.