Low-Temperature Rapid Synthesis and Superconductivity of Fe-Based Oxypnictide Superconductors

Details Low-Temperature Rapid Synthesis and Superconductivity of Fe-Based Oxypnictide Superconductors Low-Temperature Rapid Synthesis and Superconductivity of Fe-Based Oxypnictide Superconductors

2010-04-07

arxiv.org/abs/1004.0988v1

J. AM. CHEM. SOC. 9 VOL. 132, NO. 10, 2010 3261

Physics

Condensed Matter

Superconductivity

2 pages,2 figures, 1 table

Scientific paper

10.1021/ja100055k

we were able to develop a novel method to synthesize Fe-based oxypnictide
superconductors. By using LnAs and FeO as the starting materials and a
ball-milling process prior to solid-state sintering, Tc as high as 50.7 K was
obtained with the sample of Sm 0.85Nd0.15FeAsO0.85F0.15 prepared by sintering
at temperatures as low as 1173 K for times as short as 20 min.

Affiliated with

Also associated with

No associations

Rating

Low-Temperature Rapid Synthesis and Superconductivity of Fe-Based Oxypnictide Superconductors does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with Low-Temperature Rapid Synthesis and Superconductivity of Fe-Based Oxypnictide Superconductors, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Low-Temperature Rapid Synthesis and Superconductivity of Fe-Based Oxypnictide Superconductors will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFWR-SCP-O-396318