The powder-in-tube MgB2 wires were prepared by high energy milling of Mg and B powder. The powder was not mechanically alloyed for 2h short milling time. However, the MgB2 grains in wires are very small (20 100nm) and resembled to the dimple after post-heat treatment. The clear evidence for transcrystlline fracture is observed. It indicated that the grain connection was greatly improved and the fluxing pinning was significantly enhanced. Another point to view is no intermediate annealing was adopted during the whole rolling process. The influence of the post-heat treatment on the transport current density was studied. Despite the lower Tc of about 35K, the transport current density reaches to 3X10E4A/cm2 at 15K and 3.5T for 700 sintered wires.
Chen Shing-Kuo
Feng Yangyue
Li Chong Sheng
Li Jr-Shin
Lu Yu-Feng
No associations
LandOfFree
Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.
If you have personal experience with Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires will most certainly appreciate the feedback.
Profile ID: LFWR-SCP-O-152131