Oxygen nonstoichiometry, electrical conductivity and thermal expansion of La2 xSrxNiO4-\delta phases with high levels of strontium substitution (1 =< x =< 1.4) have been investigated in air and oxygen atmosphere in the temperature range 20-1050 degrees C. These phases retain the K2NiF4-type structure of La2NiO4 (tetragonal, space group I4/mmm). The oxygen vacancy fraction was determined independently from thermogravimetric and neutron diffraction experiments, and is found to increase considerably on heating. The electrical resistivity, thermal expansion and cell parameters with temperature show peculiar variations with temperature, and differ notably from La2NiO4$\pm$\delta in this respect. These variations are tentatively correlated with the evolution of nickel oxidation state, which crosses from a Ni3+/Ni4+ to a Ni2+/Ni3+ equilibrium on heating.
Makhnach Leonid V.
Pankov Vladimir V.
Strobel Pierre
No associations
LandOfFree
High-temperature oxygen non-stoichiometry, conductivity and structure in strontium-rich nickelates La2-xSrxNiO4-δ(x = 1 and 1.4) does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.
If you have personal experience with High-temperature oxygen non-stoichiometry, conductivity and structure in strontium-rich nickelates La2-xSrxNiO4-δ(x = 1 and 1.4), we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High-temperature oxygen non-stoichiometry, conductivity and structure in strontium-rich nickelates La2-xSrxNiO4-δ(x = 1 and 1.4) will most certainly appreciate the feedback.
Profile ID: LFWR-SCP-O-348836