High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route

Details High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route

2002-04-22

arxiv.org/abs/cond-mat/0204472v1

Physics

Condensed Matter

Superconductivity

Scientific paper

10.1063/1.1506184

Bulk samples of MgB2 were prepared with 5, 10, and 15% wt.% Y2O3 nanoparticles added using a simple solid-state reaction route. Transmission electron microscopy (TEM) showed a fine nanostructure consisting of ~3-5 nm YB4 nanoparticles embedded within MgB2 grains of ~400 nm size. Compared to an undoped control sample, an improvement in the in-field critical current density Jc was observed, most notably for 10% doping. At 4.2K, the lower bound Jc value was ~2x105A.cm-2 at 2T. At 20K, the corresponding value was ~8x104A.cm-2. Irreversibility fields were ~11.5 T at 4.2K and 5.5T at 20K, compared to ~4T and ~8T, respectively, for high-pressure synthesized bulk samples.

Affiliated with

Also associated with

No associations

Rating

High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFWR-SCP-O-402913