Growth of Epitaxial MgB2 Thick Films with Columnar Structures by Using HPCVD

Physics – Condensed Matter – Superconductivity

Scientific paper

Rate now

  [ 0.00 ] – not rated yet Voters 0   Comments 0

Details

10 pages including 6 figures

Scientific paper

Epitaxial MgB2 thick films were grown on Al2O3 substrates at 600 oC by using the hybrid physical chemical vapor deposition (HPCVD) technique. In order to obtain a high magnesium vapor pressure around the substrates, we used a special susceptor having a susceptor cap and achieved a very high growth rate of 0.17 um/min. Hexgonal-shaped columnar structures were observed by cross-sectional and planar view transmission electron microscope (TEM) images. For the 1.7-um-thick film, the Tc was observed to be 40.5 K with a Jc of 1.5 x 10^6 A/cm^2 at 30 K. The vortex pinning mechanism by intercolumnar boundaries will be discussed.

No associations

LandOfFree

Say what you really think

Search LandOfFree.com for scientists and scientific papers. Rate them and share your experience with other people.

Rating

Growth of Epitaxial MgB2 Thick Films with Columnar Structures by Using HPCVD does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with Growth of Epitaxial MgB2 Thick Films with Columnar Structures by Using HPCVD, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Growth of Epitaxial MgB2 Thick Films with Columnar Structures by Using HPCVD will most certainly appreciate the feedback.

Rate now

     

Profile ID: LFWR-SCP-O-22715

  Search
All data on this website is collected from public sources. Our data reflects the most accurate information available at the time of publication.