Effect of oxygen incorporation on normal and superconducting properties of MgB2 films

Details Effect of oxygen incorporation on normal and superconducting properties of MgB2 films Effect of oxygen incorporation on normal and superconducting properties of MgB2 films

2008-09-12

arxiv.org/abs/0809.2297v1

Physics

Condensed Matter

Superconductivity

10 pages, 3 figures

Scientific paper

10.1063/1.3049618

Oxygen was systematically incorporated in MBE grown MgB2 films using in-situ post-growth anneals in an oxygen environment. Connectivity analysis in combination with measurements of the critical temperature and resistivity indicate that oxygen is distributed both within and between the grains. High values of critical current densities in field (~4x10^5 A/cm^2 at 8 T and 4.2 K), extrabolated critical fields (>45 T) and slopes of critical field versus temperature (1.4 T/K) are observed. Our results suggest that low growth temperatures (300oC) and oxygen doping (>0.65%) can produce MgB2 with high Jc values in field and Hc2 for high-field magnet applications.

Affiliated with

Also associated with

No associations

Rating

Effect of oxygen incorporation on normal and superconducting properties of MgB2 films does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with Effect of oxygen incorporation on normal and superconducting properties of MgB2 films, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Effect of oxygen incorporation on normal and superconducting properties of MgB2 films will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFWR-SCP-O-603588