Core pinning by intragranular nanoprecipitates in polycrystalline MgCNi_3

Details Core pinning by intragranular nanoprecipitates in polycrystalline MgCNi_3 Core pinning by intragranular nanoprecipitates in polycrystalline MgCNi_3

2001-08-24

arxiv.org/abs/cond-mat/0108397v3

Physics

Condensed Matter

Superconductivity

5 pages, 6 figures, submitted to PRL

Scientific paper

10.1103/PhysRevB.65.214518

The nanostructure and magnetic properties of polycrystalline MgCNi_3 were studied by x-ray diffraction, electron microscopy, and vibrating sample magnetometry. While the bulk flux-pinning force curve F_p(H) indicates the expected grain-boundary pinning mechanism just below T_c = 7.2 K, a systematic change to pinning by a nanometer-scale distribution of core pinning sites is indicated by a shift of F_p(H) with decreasing temperature. The lack of scaling of F_p(H) suggests the presence of 10 to 20% of nonsuperconducting regions inside the grains, which are smaller than the diameter of fluxon cores 2xi at high temperature and become effective with decreasing temperature when xi(T) approaches the nanostructural scale. Transmission electron microscopy revealed cubic and graphite nanoprecipitates with 2 to 5 nm size, consistent with the above hypothesis since xi(0) = 6 nm. High critical current densities, more than 10^6 A/cm^2 at 1 T and 4.2 K, were obtained for grain colonies separated by carbon. Dirty-limit behavior seen in previous studies may be tied to electron scattering by the precipitates, indicating the possibility that strong core pinning might be combined with a technologically useful upper critical field if versions of MgCNi_3 with higher T_c can be found.

Affiliated with

Also associated with

No associations

Rating

Core pinning by intragranular nanoprecipitates in polycrystalline MgCNi_3 does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with Core pinning by intragranular nanoprecipitates in polycrystalline MgCNi_3, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Core pinning by intragranular nanoprecipitates in polycrystalline MgCNi_3 will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFWR-SCP-O-200221