A study of uranium-based multilayers: II. Magnetic properties

Details A study of uranium-based multilayers: II. Magnetic properties A study of uranium-based multilayers: II. Magnetic properties

2007-04-30

arxiv.org/abs/0704.3970v1

Physics

Condensed Matter

Materials Science

18 pages, 8 figures, submitted to J. Phys.: Condens. Matter

Scientific paper

10.1088/0953-8984/20/21/215230

SQUID magnetometry and polarised neutron reflectivity measurements have been employed to characterise the magnetic properties of U/Fe, U/Co and U/Gd multilayers. The field dependence of the magnetisation was measured at 10K in magnetic fields from -70kOe to 70kOe. A temperature dependent study of the magnetisation evolution was undertaken for a selection of U/Gd samples. PNR was carried out in a field of 4.4kOe for U/Fe and U/Co samples (at room temperature) and for U/Gd samples (at 10K). Magnetic 'dead' layers of about 15 Angstrom were observed for U/Fe and U/Co samples, consistent with a picture of interdiffused interfaces. A large reduction in the magnetic moment, constant over a wide range of Gd layer thicknesses, was found for the U/Gd system (about 4 Bohr magnetons compared with 7.63 for the bulk metal). This could be understood on the basis of a pinning of Gd moments arising from a column-like growth mechanism of the Gd layers. A study of the effective anisotropy suggests that perpendicular magnetic anisotropy could occur in multilayers consisting of thick U and thin Gd layers. A reduction in the Curie temperature was observed as a function of Gd layer thickness, consistent with a finite-size scaling behaviour.

Affiliated with

Also associated with

No associations

Rating

A study of uranium-based multilayers: II. Magnetic properties does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with A study of uranium-based multilayers: II. Magnetic properties, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and A study of uranium-based multilayers: II. Magnetic properties will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFWR-SCP-O-415585