We fabricated FeTe0.5Se0.5 superconducting wires using ex-situ Powder-in-tube method with an Fe sheath. It was amazing that superconducting current was observed in the as-drawn wire without any heat treatments. By heat treatment at 200C for 2 hours, Tczero and Jc at 4.2 K were enhanced up to 9.1 K and 64.1 A/cm2 (Ic = 182.6 mA), respectively. Furthermore, the Jc of FeTe0.5Se0.5 wire heat treated at 200C for 2 hours was not much sensitive to the applied magnetic fields. Therefore, FeTe0.5Se0.5 wires have a great potential for applications.
Deguchi Keita
Kumakura Hiroaki
Mizuguchi Yoshikazu
Ozaki Taisuke
Takano Yasushi
No associations
LandOfFree
Microstructure and transport properties of FeTe0.5Se0.5 superconducting wires fabricated by ex-situ Powder-in-tube process does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.
If you have personal experience with Microstructure and transport properties of FeTe0.5Se0.5 superconducting wires fabricated by ex-situ Powder-in-tube process, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Microstructure and transport properties of FeTe0.5Se0.5 superconducting wires fabricated by ex-situ Powder-in-tube process will most certainly appreciate the feedback.
Profile ID: LFWR-SCP-O-479562