7 pages, 1 Fig. 2 tables, minor editiorial revision
Scientific paper
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires were then rolled into tapes 2.56 x 0.32 mm2, with a total superconducting cross section of 0.2319 mm2. Transport measurements were performed using a standard four-point technique at T = 4.2 K (in liquid helium) and at self field. Three samples were prepared, with heat treatments of 900C for 1, 2, and 3 h under 1/3 at Ar. Measured values of transport current were 4.7, 7.5, and 1.1 x 104 A/cm2, respectively, at 4.2 K and self field. M-H loops taken on the sample HT for 1 h showed magnetic Jcs of 4.2 x 104 A/cm2 at 4.2 K and 1 T, indicating that the material had reasonably well connected grains.
Collings E. W.
Lee Edward
Peng Xinhua
Sumption M. D.
Tomsic Matija
No associations
LandOfFree
Transport Current in MgB2 based Superconducting Strand at 4.2 K and Self-Field does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.
If you have personal experience with Transport Current in MgB2 based Superconducting Strand at 4.2 K and Self-Field, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Transport Current in MgB2 based Superconducting Strand at 4.2 K and Self-Field will most certainly appreciate the feedback.
Profile ID: LFWR-SCP-O-178739