Proc. SPIE Vol. 3444, p. 543-550, X-Ray Optics, Instruments, and Missions, Richard B. Hoover; Arthur B. Walker; Eds.
Physics
Optics
Scientific paper
We report a study of the residual stresses and residual stress relaxation in Mo/Si and Mo(subscript 2)C/Si EUV multilayers. The multilayers were fabricated by magnetron sputter deposition, and stress measured using the substrate curvature laser scanning technique. It was found that Mo(subscript 2)C/Si multilayers exhibit higher compressive stress than Mo/Si of comparable period and layer thickness ratio. The multilayers sputtered at 0.5 mT Ar pressure have higher compressive stress than those sputtered at 2 mT Ar pressure. The data indicate that the residual stresses in the multilayers are primarily determined by the Si layers. Annealing of the multilayers at a heating rate of 5 degrees C/minute as well as at a fixed temperature results in a reduction of the compressive stresses. Near zero stress is achieved after annealing at 300 degrees C. The time dependence of the residual stress decrease during isothermal annealing was found to fit best to a bimolecular viscous flow model of defect annihilation in the amorphous Si layers. The relationships between the effects of annealing on the multilayer microstructure and the observed stress reduction are discussed.
Barbee Troy W.
Nguyen Thinh Duc
No associations
LandOfFree
Residual stresses in Mo/Si and Mo2C/Si multilayers does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.
If you have personal experience with Residual stresses in Mo/Si and Mo2C/Si multilayers, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and Residual stresses in Mo/Si and Mo2C/Si multilayers will most certainly appreciate the feedback.
Profile ID: LFWR-SCP-O-805351