High temperature calorimetry of sulfide systems. I. Thermochemistry of liquid and solid phases of Ni + S

Details High temperature calorimetry of sulfide systems. I. Thermochemistry of liquid and solid phases of Ni + S High temperature calorimetry of sulfide systems. I. Thermochemistry of liquid and solid phases of Ni + S

Aug 1986

adsabs.harvard.edu/cgi-bin/nph-data_query?bibcode=1986gecoa..50.1633c&link_type=abstract

Geochimica et Cosmochimica Acta, vol. 50, Issue 8, pp.1633-1641

Computer Science

2

Scientific paper

An experimental arrangement suitable for application of high temperature calorimetry to liquid sulfide systems has been developed. Using this approach, we have measured the integral enthalpies of mixing of Ni + NiS at 1100 K to form liquid alloys with compositions from X Nis = 0.576 to X Nis = 0.754. Partial enthalpies of the two components also were measured. After correcting for the enthalpies of fusion of Ni and NiS at 1100 K, the results of all measurements can be represented by an analytical expression which reflects subregular behavior of the mixing enthalpies H mix l -1 = X Nis 2 X Ni A + X Nis X NiS 2 B with A = -97.712 kJ mol -1 and B = -4.772 kJ mol -1 . The standard enthalpies of formation of the high and low temperature forms of NiS were evaluated from the calorimetrically measured enthalpy change associated with the reaction between nickel and sulfur at 1021 K. The standard enthalpies of formation of Ni 3 S 2 (heazlewoodite), Ni 7 S 6 and Ni 0.958 S were determined from the enthalpy changes of reactions in which the compounds were formed from NiS and Ni at 873 K and 833 K. The standard enthalpy of formation of NiS 2 (vaesite) was obtained from the enthalpy change of the reaction of NiS 2 with Ni to give NiS at 873 K. The following values are reported for the standard enthalpies of formation of the phases studied (in kJ mol -1 ): H f , NiS ( HT ) 0 = -88.1 ± 1.0 H f , Ni 0.958 S 0 = -93.2 ± 0.7 H f , Ni 7 S 6 0 = -582.8 ± 5.7 H f , NiS ( LT ) 0 = -91.0 ± 1.0 H f , Ni 3 S 2 ( LT ) 0 = -217.2 ± 1.6 H f , NiS 2 0 = -124.9 ± 1.0.

Affiliated with

Also associated with

No associations

Rating

High temperature calorimetry of sulfide systems. I. Thermochemistry of liquid and solid phases of Ni + S does not yet have a rating. At this time, there are no reviews or comments for this scientific paper.

If you have personal experience with High temperature calorimetry of sulfide systems. I. Thermochemistry of liquid and solid phases of Ni + S, we encourage you to share that experience with our LandOfFree.com community. Your opinion is very important and High temperature calorimetry of sulfide systems. I. Thermochemistry of liquid and solid phases of Ni + S will most certainly appreciate the feedback.

Rate now

Comments { 0 }

Profile ID: LFWR-SCP-O-892688